Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| | | 按重量计算的混合比:110,按容量计算的混合比:96 |
| | | 按重量计算的混合比:100,按容量计算的混合比:100 |
| | | 26 wk |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792,ASTMD1622 | 1.04 g/cm³ |
| Shrinkage rate | | 内部方法 | 0.80到0.90 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 55 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| flammability | | FMVSS302 | Pass |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| HeatSag | | ASTMD3769 | 1.70 cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| | ASTMD1044 | 200 mg |
| Flexural modulus | | ASTMD790 | 724 MPa |
| Flexural modulus | | ASTMD790 | 345 MPa |
| Flexural modulus | | ASTMD790 | 124 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 670 J/m |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD412 | 24.1 MPa |
| elongation | | ASTMD412 | 200 % |
| tear strength | | ASTMD624 | 92.8 kN/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD696 | 1.1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.