PP Homopolymer TRANSMARE® 35HNF50-0.001
0
- Properties:FillerBambooFiber50%Filler by weight
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.02 g/cm³ | |
| melt mass-flow rate | ISO1133 | 2.2 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO868 | 78 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179/1U | 7.3 kJ/m² | |
| ISO179/1U | 9.2 kJ/m² | ||
| Impact strength of cantilever beam gap | ISO180/1A | 3.6 kJ/m² | |
| ISO180/1U | 9.3 kJ/m² | ||
| Charpy Notched Impact Strength | ISO179/1A | 2.5 kJ/m² | |
| ISO179/1A | 3.0 kJ/m² | ||
| ISO179/1A | 3.4 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | ISO527-2/50 | 1.6 % | |
| Flexural modulus | ISO178 | 4960 MPa | |
| Bending stress | ISO178 | 68.0 MPa | |
| Tensile stress | ISO527-2/50 | 43.0 MPa | |
| Tensile modulus | ISO527-2/1 | 5050 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO306/A | 163 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.