ABS T50 XF

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO1183	1.11 g/cm³
MeltViscosity		ISO11443-A	190 Pa·s
Melt volume flow rate		ISO1133	19.0 cm³/10min
Shrinkage rate		ISO2577	0.55to0.75 %
Shrinkage rate	Shrinkage rate		ISO2577	0.55to0.75 %
Water absorption rate		ISO62	0.70 %
Water absorption rate	Water absorption rate		ISO62	0.20 %

flammability	Test Condition	Test Method	Test Result
FlameRating		UL94	HB

Mechanical properties	Test Condition	Test Method	Test Result
Tensile strain		ISO527-2/50	4.5 %
Tensile strain	Tensile strain		ISO527-2/50	>50 %
Tensile modulus		ISO527-2/1	2100 MPa
Tensile stress		ISO527-2/50	50.0 MPa
Tensile stress	Tensile stress		ISO527-2/50	46.0 MPa

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ISO180/A	38 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO180/A	45 kJ/m²
		ISO180	NoBreak
			ISO180	NoBreak

Electrical performance	Test Condition	Test Method	Test Result
Surface Resistivity		IEC60093	1E+17 ohms
Volume resistivity		IEC60093	1E+16 ohms·cm
dielectric strength		IEC60243-1	40 kV/mm
		IEC60250	3.10
			IEC60250	3.00
Dissipation Factor		IEC60250	2.5E-03
Dissipation Factor	Dissipation Factor		IEC60250	9E-03
CTI		IEC60112	250 V

Thermal performance	Test Condition	Test Method	Test Result
		ISO11359-2	8.5E-05 cm/cm/°C
			ISO11359-2	8.5E-05 cm/cm/°C
				ISO75-2/B	120 °C
					ISO75-2/A	99.0 °C
vicat		ISO306/B50	113 °C
vicat	vicat		ISO306/B120	115 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.