Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | 0.35 % |
| density | | ISO1183 | 1.29 g/cm³ |
| melt mass-flow rate | | ISO1133 | 28到38 g/10min |
| Shrinkage rate | | ISO294-4,ISO2577 | 1.0 % |
| Shrinkage rate | | ISO294-4,ISO2577 | 0.90 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 2270 MPa |
| Tensile stress | | ISO527-2 | 70.0 MPa |
| Tensile strain | Yield | ISO527-2 | 7.8 % |
| Flexural modulus | | ISO178 | 2400 MPa |
| Bending stress | | ISO178 | 105 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/A | 68 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC60243-1 | 44 kV/mm |
| dielectric constant | | IEC60250 | 3.80 |
| dielectric constant | | IEC60250 | 3.70 |
| Dissipation Factor | | IEC60250 | 1.5E-03 |
| Dissipation Factor | | IEC60250 | 8.6E-03 |
| CTI | | IEC60112 | 150 V |
| Surface Resistivity | | IEC60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO75-2/A | 196 °C |
| Glass Transition Temperature | | ISO11357-2,DSC | 220 °C |
| | ISO11359-2 | 5.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.