Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.60 % |
| Shrinkage rate | | ISO 294-4 | 0.10 % |
| Water absorption rate | | ISO 62 | 2.3 % |
| Water absorption rate | | ISO 62 | 1.1 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 170 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | UL 94 | HB |
| ISO Type | | ISO 1874 | PA1010 + X. MH. 16-110. GF 30 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 11000 Mpa |
| tensile strength | | ISO 527-2 | 115 Mpa |
| Tensile strain | | ISO 527-2 | 2.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 40 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 40 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | -- ohms |
| Volume resistivity | | IEC 60093 | 1.0E+12 ohms·cm |
| dielectric strength | | IEC 60243-1 | 40 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 165 °C |
| Heat distortion temperature | | ISO 75-2/C | 110 °C |
| Continuous use temperature | | ISO 2578 | 90.0 to 110 °C |
| Continuous use temperature | | 内部方法 | 150 °C |
| melting temperature | | ISO 11357-3 | 200 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 3.0E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 7.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.