Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 0.50 % |
| Water absorption rate | | ISO62 | 0.20 % |
| water content | | ISO15512 | <0.080 % |
| Shrinkage rate | | 内部方法 | 1.1 % |
| other | Test Condition | Test Method | Test Result |
|---|
| | | 加纤20% 增强级 |
| purpose | | | 电工电子器材 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 6000 Mpa |
| Tensile stress | | ISO527-2 | 105 Mpa |
| Tensile strain | | ISO527-2 | 3.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| | ISO180/1U | 45 kJ/m² |
| | ISO180/1U | 50 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+14 ohms |
| Volume resistivity | | IEC60093 | 1E+16 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 215 °C |
| | ISO75-2/A | 195 °C |
| vicat | | ISO306/B | 205 °C |
| melting temperature | | ISO11357-3 | 225 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.