| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.18 g/cm³ |
| Shrinkage rate | | ASTMD4802 | 2.2 % |
| Shrinkage rate | | ASTMD4802 | 1.9 % |
| Water absorption rate | | ASTMD570 | 0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 88 |
| Barcol Hardness | | ASTMD2583 | 40 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| HotFormingTemperature | | 内部方法 | 160到182 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTMD790 | 94.5 MPa |
| Tensile modulus | | ASTMD638 | 2870 MPa |
| tensile strength | | ASTMD638 | 57.0 MPa |
| elongation | | ASTMD638 | 14 % |
| Flexural modulus | | ASTMD790 | 2730 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| CharpyUnnotched | | ASTMD6110 | 544 J/m |
| Impact strength of cantilever beam gap | | ASTMD256A | 59 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD696 | 7.2E-05 cm/cm/°C |
| thermal stability | | ASTMD4802 | NoEffect |
| | ASTMD648 | 80.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.