PP J-740

Properties:
Characteristics
high impact strength
and high fluidity
Usages:
Widely used in the production of automotive parts
electrical equipment and parts
as well as other large-sized miscellaneous boxes
Compare

Technical Data Sheet

Basic performance	Test Condition	Test Method	Test Result
melt mass-flow rate			优级品｜25 g/10min
	melt mass-flow rate			一级品｜25 g/10min
	melt mass-flow rate	melt mass-flow rate			合格品｜25 g/10min

Mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap			一级品｜≥80 J/M
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap			合格品｜≥80 J/M
tensile strength			优级品｜≥22 MPa
	tensile strength			一级品｜≥22 MPa
	tensile strength	tensile strength			合格品｜≥22 MPa
Flexural modulus			优级品｜≥1000 MPa
	Flexural modulus			一级品｜≥1000 MPa
	Flexural modulus	Flexural modulus			合格品｜≥1000 MPa
Impact strength of cantilever beam gap			优级品｜≥80 J/M

Other performance	Test Condition	Test Method	Test Result
cleanliness			优级品｜0-5 个/kg
	cleanliness			一级品｜6-10 个/kg
		cleanliness			合格品｜11-20 个/kg
		cleanliness	cleanliness			合格品｜11-20 个/kg
ash content			优级品｜≤0.04 %
	ash content			一级品｜≤0.04 %
	ash content	ash content			合格品｜≤0.04 %
cleanliness			优级品｜0-5 个/kg
cleanliness	cleanliness			一级品｜6-10 个/kg

Thermal performance	Test Condition	Test Method	Test Result
vicat			优级品｜140 ℃
	vicat			一级品｜140 ℃
	vicat	vicat			合格品｜140 ℃

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.