Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 36 g/10min |
| Shrinkage rate | | 内部方法 | 0.60 % |
| Shrinkage rate | | 内部方法 | 0.50 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTM D542 | 1.540 |
| transmissivity | | ASTM D1003 | 90.0 % |
| Haze ratio | | ASTM D1003 | <0.50 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ASTM D256 | 10.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 60.0 Mpa |
| elongation | | ASTM D638 | 3.0 % |
| Flexural modulus | | ASTM D790 | 3200 Mpa |
| bending strength | | ASTM D790 | 100 Mpa |
| film | Test Condition | Test Method | Test Result |
|---|
| Water Vapor Transmission Rate | | ASTMF1249 | 0.090 g·mm/m²/atm/24hr |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 125 °C |
| Glass Transition Temperature | | 内部方法 | 135 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 7E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTM D696 | 6E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.