PA66 13T1 BK DUPONT USA

Form：Granules | Grade：Injection grade

Properties:

Thermal stability

Typical Applications:

Automotive interior partsElectrical applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive interior parts \| Electrical applications
Properties:	Thermal stability

Certificates

No Data...

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23℃,Equilibrium	ISO 62	DAM｜1.6	%
	Water absorption rate	23℃,Equilibrium	ISO 62	50%RH｜-	%
		Water absorption rate	23℃,Saturation	ISO 62	DAM｜6	%
		Water absorption rate	Water absorption rate	23℃,Saturation	ISO 62	50%RH｜-	%
density			DAM｜1.35	g/ml
density	density			50%RH｜1.35	g/ml
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	Notched-30℃		DAM｜6.0	kJ/m²
	Charpy Notched Impact Strength	Notched-30℃		50%RH｜5.0	kJ/m²
		Charpy Notched Impact Strength	Unnotched-40℃	ISO 179	DAM｜130	kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	Unnotched-40℃	ISO 179	50%RH｜120	kJ/m²
tensile strength	5mm/min	ISO 527	DAM｜72	Mpa
tensile strength	tensile strength	5mm/min	ISO 527	50%RH｜50	Mpa
Charpy Notched Impact Strength	Notched23℃	ISO 179	DAM｜8.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Notched23℃	ISO 179	50%RH｜13.0	kJ/m²
Rockwell hardness		ISO 2039/2	DAM｜118	Scale R
Rockwell hardness	Rockwell hardness		ISO 2039/2	50%RH｜-	Scale R
Charpy Notched Impact Strength	Unnotched23℃	ISO 179	DAM｜NB	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Unnotched23℃	ISO 179	50%RH｜NB	kJ/m²
Elongation at Break	5mm/min	ISO 527	DAM｜18	%
Elongation at Break	Elongation at Break	5mm/min	ISO 527	50%RH｜47	%
Impact strength of cantilever beam gap	-30℃	ISO 180	DAM｜4.6	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30℃	ISO 180	50%RH｜3.7	kJ/m²
Young's modulus	1mm/min		DAM｜4000	Mpa
Young's modulus	Young's modulus	1mm/min		50%RH｜1500	Mpa
Rockwell hardness		ISO 2039/2	DAM｜80	Scale M
Rockwell hardness	Rockwell hardness		ISO 2039/2	50%RH｜-	Scale M
Impact strength of cantilever beam gap	23℃	ISO 180	DAM｜10.7	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃	ISO 180	50%RH｜13	kJ/m²
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 1218	255	°C
Melting temperature	Melting temperature		ISO 1218	255	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	Across Flow	ISO 2577	DAM｜1.6	%
	Shrinkage rate	Across Flow	ISO 2577	50%RH｜-	%
		Shrinkage rate	Flow	ISO 2577	DAM｜1.4	%
		Shrinkage rate	Shrinkage rate	Flow	ISO 2577	50%RH｜-	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1MHz	ISO 250	DAM｜200	10-4
	Dissipation factor	1MHz	ISO 250	50%RH｜650	10-4
		Dissipation factor	50Hz	IEC 250	DAM｜100	10-4
		Dissipation factor	Dissipation factor	50Hz	IEC 250	50%RH｜4500	10-4
Dielectric strength		IEC 243	DAM｜35	KV/mm
Dielectric strength	Dielectric strength		IEC 243	50%RH｜-	KV/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.