PA6 B3GK24 BK00564 BASF KOREA

Form：Granules | Grade：Injection grade

Properties:

Flame retardantOil resistantHalogen-freeFiller: glass beads fibe30% filler by weight

Typical Applications:

Electrical applicationsIndustrial machineryApplication in the automotive fieldIndustrial componentsElectrical enclosure

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical applications \| Industrial machinery \| Application in the automotive field \| Industrial components \| Electrical enclosure
Properties:	Flame retardant \| Oil resistant \| Halogen-free \| Filler: glass beads \| fibe \| 30% filler by weight

Certificates

No Data...

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
impact strength	干/湿		5/25	J
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ASTM D256	37	J/m
Charpy Notched Impact Strength	-30°C	ISO 179	5.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	5.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	39	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	40	kJ/m²
Impact strength of cantilever beam gap	-40°C	ASTM D256	32	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	+23℃,干/湿		40/90	KJ/m
Fracture stress (V=50mm/min)	干/湿		110/65	Mpa
Tensile yield stress (V=50mm/min)	干/湿		110/65	Mpa
Elongation at Break	干/湿，V=50mm/min		3.5/15	%
Charpy Notched Impact Strength	30℃干		39	KJ/m
Tensile modulus	干/湿		6000/3000	Mpa
Ball Pressure Test	干/湿		170/120	Mpa
Charpy Notched Impact Strength	30℃，干/湿		5	KJ/m
Impact strength of cantilever beam gap	+23℃，干/湿		5/8.5	KJ/m
Elongation at Break	干/湿，V=50mm/min		3.5/15	%
Tensile creep modulus	1000h,湿		2000	Mpa
Tensile modulus	23°C	ISO 527-2	6000	Mpa
tensile strength	Break,23°C	ASTM D638	110	Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2	105	Mpa
Tensile strain	Break,23°C	ISO 527-2	3.5	%
Bending modulus	23°C	ASTM D790	4830	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
thermal conductivity	Dry		0.34	W/(m.K)
Linear coefficient of thermal expansion	（23-80）℃，Dry		3.5-4	10
Hot deformation temperature	0.45MPa负荷，Dry		215	°C
Maximum operating temperature			200	°C
specific heat	Dry		1.4	J/(g.K)
Hot deformation temperature	1.8MPa负荷，Dry		200	°C
	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	215	°C
		Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	215	°C
			Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	200	°C
			Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	200	°C
Melting temperature		ASTM D3418	220	°C
Melting temperature	Melting temperature		ISO 3146	220	°C
Linear coefficient of thermal expansion	MD	ASTME831	1E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD		3.8E-05	cm/cm/°C
RTI Elec	0.75mm	UL 746	65.0	°C
	RTI Elec	1.5mm	UL 746	65.0	°C
	RTI Elec	RTI Elec	3.0mm	UL 746	65.0	°C
RTI Imp	0.75mm	UL 746	65.0	°C
	RTI Imp	1.5mm	UL 746	65.0	°C
	RTI Imp	RTI Imp	3.0mm	UL 746	65.0	°C
RTI Str	0.75mm	UL 746	65.0	°C
	RTI Str	1.5mm	UL 746	65.0	°C
	RTI Str	RTI Str	3.0mm	UL 746	65.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.34	g/cm³
density	density		ISO 1183	1.34	g/cm³
Melt Volume Flow Rate (MVR)	275°C/5.0kg	ISO 1133	70.0	cm3/10min
Shrinkage rate	MD：3.18mm		0.40	%
Water absorption rate	Saturation	ASTM D570	6.6	%
	Water absorption rate	Saturation,23°C	ISO 62	6.6	%
		Water absorption rate	Equilibrium,50%RH	ASTM D570	2.0	%
		Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.0	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the Leakage Traceability Index (CTI)	干/湿		CTI 425
bending strength	干/湿		175/100	Mpa
Volume resistivity	干/湿		10	Ω.cm
Surface resistivity	干/湿		10	Ω
Dielectric strength	K20/P50，干/湿		135/53	KV/mm
Loss angle	1MHz，干/湿		0.02/0.07
Dielectric constant	1MHz，干/湿		3.9/4.6	J/(g.K)
Volume resistivity	1.50mm	ASTM D257	1E+15	ohms·cm
Volume resistivity	Volume resistivity		IEC 60093	1E+15	ohms·cm
Dielectric constant	1MHz	IEC 60250	3.90
Dissipation factor	1MHz	IEC 60250	0.020
Compared to the anti leakage trace index		IEC 60112	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.