Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.85到1.95 g/cm³ |
| Apparent density | | ISO60 | 0.60到0.80 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.30到0.50 % |
| Water absorption rate | | ISO62 | <0.10 % |
| PostShrinkage | | ISO2577 | <0.050 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 960 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CompressionMoldingPressure | | | >20.0 MPa |
| CompressionMoldingTemperature | | | 165到180 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | Injection | ISO178 | 18000到22000 MPa |
| Bending stress | Compression Molded | ISO178 | 150到180 MPa |
| Bending stress | Injection | ISO178 | 220到240 MPa |
| compression stress | | ISO604 | 280到330 MPa |
| Tensile modulus | Compression Molded | ISO527-2 | 14000到18000 MPa |
| Tensile modulus | Injection | ISO527-2 | 16000到20000 MPa |
| Tensile stress | | ISO527-2 | 80.0到100 MPa |
| Tensile stress | Injection | ISO527-2 | 120到140 MPa |
| Flexural modulus | Compression Molded | ISO178 | 16000到18000 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO179/1eA | 4.0到6.0 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO179/1eA | 5.0到7.0 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO179/1eU | 8.0到10 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO179/1eU | 12到14 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1.0E+10到1.0E+11 ohms |
| Volume resistivity | | IEC60093 | 1.0E+12到1.0E+13 ohms·cm |
| dielectric strength | | IEC60243-1 | 20到30 kV/mm |
| | IEC60250 | 6.008.00 |
| | IEC60250 | 4.006.00 |
| Dissipation Factor | | IEC60250 | 0.10到0.20 |
| Dissipation Factor | | IEC60250 | 0.020到0.030 |
| arc resistance | | ASTMD495 | PLC 4 |
| CTI | | IEC60112 | >175 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | >200 °C |
| | ISO75-2/C | 160到180 °C |
| | ISO11359-2 | 1.5E-5到2.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.40到0.60 W/m/K |
| maximum service temperature | | IEC60216 | 230 °C |
| maximum service temperature | | IEC60216 | 150 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.