Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.42 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.15 % |
| Shrinkage rate | | ISO 294-4 | 0.60 % |
| Water absorption rate | | ISO 62 | 0.11 % |
| Flame retardancy | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL -94 | V-0 6.00mm |
| UL flame retardant rating | | UL -94 | V-2 1.50mm |
| UL flame retardant rating | | UL -94 | V-0 3.00mm |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 75 M（Scale） |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation at break | | ISO 527-2 | 4.0 % |
| Tensile modulus | | ISO 527-2 | 7900 MPa |
| bending strength | | ISO 178 | 180 MPa |
| Flexural modulus | | ISO 178 | 7900 MPa |
| Charpy Notched Impact Strength | | ISO 179/1eA | 17 kJ/m² |
| tensile strength | | ISO 527-2 | 130 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | IEC 60250 | 2.95 1MHz |
| Dissipation Factor | | IEC 60250 | 3.10 100Hz |
| Dissipation Factor | | IEC 60250 | 2.95 1MHz |
| Volume resistivity | | IEC 60093 | 1E+33 Ω.cm |
| dielectric strength | | IEC 60243-1 | 15 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/Af | 147 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 2.3E-05 cm/cm／°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.