PC/ABS CX7240-7T1D193 SABIC INNOVATIVE SHANGHAI

Form：Granules

Properties:

Middle flowChemical resistanceRapid prototyping

Typical Applications:

Office equipmentElectronic and electrical enclosureCommunication equipmentThin walled products

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Office equipment \| Electronic and electrical enclosure \| Communication equipment \| Thin walled products
Properties:	Middle flow \| Chemical resistance \| Rapid prototyping

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	-30°C10	ISO 180/1A	10	kJ/m²
	Impact strength of cantilever beam gap	-30°C9	ISO 180/1A	10	kJ/m²
		Impact strength of cantilever beam gap	23°C	ASTM D256	700	J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ASTM D256	180	J/m
Charpy Notched Impact Strength	23°C7	ISO 179/1eA	20	kJ/m²
	Charpy Notched Impact Strength	23°C8	ISO 179/1eA	22	kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C7	ISO 179/1eA	10	kJ/m²
Impact strength of cantilever beam gap	23°C9	ISO 180/1A	25	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C10	ISO 180/1A	20	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	65.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index		ISO 4589-2	35	%
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	800	°C
UL flame retardant rating	0.60mm	UL 94	V-1
	UL flame retardant rating	0.75mm	UL 94	V-0
		UL flame retardant rating	1.5mm	UL 94	5VB
		UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA
Burning wire flammability index	0.75mm13	IEC 60695-2-12	960	°C
Burning wire flammability index	Burning wire flammability index	0.75mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.75mm13	IEC 60695-2-13	775	°C
	Hot filament ignition temperature	1.0mm	IEC 60695-2-13	825	°C
		Hot filament ignition temperature	1.5mm13	IEC 60695-2-13	775	°C
		Hot filament ignition temperature	Hot filament ignition temperature	3.0mm13	IEC 60695-2-13	775	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Break	ASTM D638	58.0	Mpa
	tensile strength	Yield	ISO 527-2/50	65.0	Mpa
	tensile strength	tensile strength	Yield	ASTM D638	65.0	Mpa
Tensile modulus		ISO 527-2/1	2600	Mpa
Tensile modulus	Tensile modulus		ASTM D638	2600	Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	104	Mpa
bending strength	bending strength		ISO 178	96.0	Mpa
Bending modulus		ISO 178	2500	Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	2500	Mpa
Tensile strain	Break	ISO 527-2/50	90	%
elongation	Break	ASTM D638	100	%
Tensile strain	Yield	ISO 527-2/50	4.0	%
elongation	Yield	ASTM D638	4.1	%
tensile strength	Break	ISO 527-2/50	50.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	100	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	89.0	°C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	99.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	93.0	°C
RTI Elec		UL 746	90.0	°C
Vicat softening temperature		ASTM D152512	110	°C
	Vicat softening temperature	--	ISO 306/B50	110	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	113	°C
Ball Pressure Test	75°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.5E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	7.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	7.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	7.5E-05	cm/cm/°C
thermal conductivity		ISO 8302	0.20	W/m/K
RTI Imp		UL 746	90.0	°C
RTI Str		UL 746	90.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.10	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.20	%
density		ASTM D792	1.19	g/cm³
density	density		ISO 1183	1.20	g/cm³
melt mass-flow rate	260°C/2.16kg	ASTM D1238	18	g/10min
Melt Volume Flow Rate (MVR)	260°C/2.16kg	ISO 1133	15.0	cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.40-0.60	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength	0.800mm,in Oil	IEC 60243-1	35	KV/mm
Surface resistivity		IEC 60093	>1.0E+15	ohms
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Dielectric strength	1.60mm,in Oil	IEC 60243-1	25	KV/mm
Dielectric strength	Dielectric strength	3.20mm,in Oil	IEC 60243-1	17	KV/mm
Compared to the anti leakage trace index	CTI	UL 746	PLC 3
High arc combustion index	HAI	UL 746	PLC 0
Hot wire ignition	HWI	UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC/ABS CX7240-7T1D193 SABIC INNOVATIVE SHANGHAI

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index