PA/ABS N NM-13 BASF USA

Form：Granules | Grade：Injection grade

Properties:

Low temperature resistancHigh impact resistance

Typical Applications:

Low temperature applicationssporting goods

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Low temperature applications \| sporting goods
Properties:	Low temperature resistanc \| High impact resistance

Certificates

No Data...

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Yield,23°C	ISO 527-2	3.4	%
tensile strength	Yield,23°C	ISO 527-2	35.0	Mpa
Tensile modulus		ISO 527-2	1600	Mpa
bending strength		ISO 178	50.0	Mpa
Bending modulus		ISO 178	1500	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD	ISO 11359-2	1E-04	cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	91.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	165	°C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	58.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	80.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.1	%
Shrinkage rate		ISO 294-4	0.80	%
Melt Volume Flow Rate (MVR)	240°C/10.0kg	ISO 1133	25.0	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112	PLC 0
Dissipation factor	1MHz	IEC 60250	0.015
Relative permittivity	1MHz	IEC 60250	2.90
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Surface resistivity		IEC 60093	1E+14	ohms
film	Test Condition	Test Method	Test Result	Test Unit
elongation	Break	ISO 527-3	>50	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.