POM 500T DUPONT NETHERLANDS

Form：Granules | Grade：Injection grade

Properties:

High rigiditywear resistantThermal stabilityHigh impact resistance

Typical Applications:

Automotive Applicationsfibre

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| fibre
Properties:	High rigidity \| wear resistant \| Thermal stability \| High impact resistance

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	7.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	13	kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	9.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	12	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	ISO 3795	55	mm/min
UL flame retardant rating	0.75mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	0.75mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
FMVSS flammability		FMVSS302	B
Fogging-G-value	condensate	ISO 6452	2E-04	g
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	2300	Mpa
tensile strength	Yield	ISO 527-2	54.0	Mpa
Tensile strain	Yield	ISO 527-2	17	%
Nominal tensile fracture strain		ISO 527-2	28	%
Bending modulus		ISO 178	2000	Mpa
bending strength	3.5%Strain	ISO 178	60.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	146	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	76.0	°C
Melting temperature		ISO 11357-3	178	°C
AnnealingTemperature			160	°C
AnnealingTime-Optional			30.0	min/mm
Physical properties	Test Condition	Test Method	Test Result	Test Unit
MediumDensity			1.19	g/cm³
density		ISO 1183	1.39	g/cm³
melt mass-flow rate	190°C/2.16kg	ISO 1133	12	g/10min
Shrinkage rate	TD	ISO 294-4	1.5	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.5	%
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
EmissionofOrganicCompounds		VDA277	3.40	µgC/g
Emission		VDA275	<8.00	mg/kg

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.