Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 13 g/10min |
| Melt volume flow rate | | ISO 1133 | 8.50 cm3/10min |
| Shrinkage rate | | | 0.32 % |
| Water absorption rate | | ISO 62 | 0.73 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 16000 Mpa |
| tensile strength | | ISO 527-2 | 208 Mpa |
| Tensile strain | | ISO 527-2 | 2.0 % |
| Flexural modulus | | ISO 178 | 14300 Mpa |
| bending strength | | ISO 178 | 349 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 90 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| relative permittivity | | IEC 60250 | 4.10 |
| Dissipation Factor | | IEC 60250 | 5.5E-03 |
| Dissipation Factor | | IEC 60250 | 6.7E-03 |
| relative permittivity | | IEC 60250 | 4.20 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 232 °C |
| Glass Transition Temperature | | ISO 11357-2 | 87.0 °C |
| melting temperature | | ISO 11357-3 | 257 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.1E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5.6E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare