Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO1133 | 5.00 cm3/10min |
| Shrinkage rate | | ISO294-4 | 0.40到0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 109 |
| other | Test Condition | Test Method | Test Result |
|---|
| | | 抗疲劳 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | | 5 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790/ISO 178 | 2,600 kg/cm²(MPa)[Lb/in²] |
| Charpy impact strength | | ASTM D256/ISO 179 | 28 kg·cm/cm(J/M)ft·lb/in |
| Charpy impact strength | | | 28 kJ/m² |
| Flexural modulus | | | 2600 Mpa |
| Tensile modulus | | ISO527-2 | 2350 Mpa |
| Tensile stress | | ISO527-2 | 45.0 Mpa |
| Bending modulus 2 | | ISO178 | 2600 Mpa |
| Bending stress 2 | | ISO178 | 72.0 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 5 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Combustibility (rate) | | UL94 | HB |
| | ASTM D648/ISO 75 | 83 ℃（℉） |
| | | 83 °C |
| UL flame retardant rating | | UL94 | HB |
| | ISO11359-2 | 8.5E-05 cm/cm/°C |
| | ISO75-2/Af | 83.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.