Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | | 0.70 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 1.0 % |
| Shrinkage rate | | ISO 294-4 | 0.30 % |
| Water absorption rate | | ISO 62 | 4.3 到 5.3 % |
| Water absorption rate | | ISO 62 | 0.80 到 1.2 % |
| viscosity number | | ISO 307 | 130 cm³/g |
| Mold Shrinkage - Constrained 3 | | | 0.35 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | IEC 60695-11-10, -20 | HB |
| Polymer Abbreviation | | | PA6T/6-GF35 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 12000 Mpa |
| Tensile stress | | ISO 527-2 | 210 Mpa |
| Tensile strain | | ISO 527-2 | 3.0 % |
| Tensile creep modulus | | ISO 899-1 | -- Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 100 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | -- ohms |
| Volume resistivity | | IEC 60093 | 1.0E+15 ohms·cm |
| Dielectric strength 7 | | IEC 60243-1 | 33 KV/mm |
| | IEC 60250 | 4.20 |
| Dissipation Factor | | IEC 60250 | 0.020 |
| CTI | | IEC 60112 | 600 V |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 110 °C |
| drying time | | | 8.0 hr |
| Suggested maximum moisture content | | | 0.15 % |
| Hopper temperature | | | 80 °C |
| Temperature at the rear of the barrel | | | 300 °C |
| Temperature in the middle of the barrel | | | 310 °C |
| Temperature at the front of the material cylinder | | | 320 °C |
| Spray nozzle temperature | | | 320 °C |
| Processing (melt) temperature | | | 310 到 330 °C |
| Temperature | | | 80 到 120 °C |
| Residence Time | | | < 5.0 min |
| Screw Speed | | | < 18 m/min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 75-2/A | 245 °C |
| melting temperature | | ISO 11357-3 | 295 °C |
| | ISO 11359-2 | 1.5E-5 cm/cm/°C |
| | ISO 11359-2 | 5.0E-5 到 6.0E-5 cm/cm/°C |
| specific heat | | | 1300 J/kg/°C |
| thermal conductivity | | DIN 52612 | 0.28 W/m/K |
| 温度指数 - at 50% loss of tensile strength | | IEC 60216 | 160 °C |
| 温度指数 - at 50% loss of tensile strength | | IEC 60216 | 135 °C |
| Maximum operating temperature - short cycle operation | | | 270 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.