Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD | ISO294-4 | 1.8 | % |
| Shrinkage rate | MD | ISO294-4 | 2.0 | % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 1.3 | % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.40 | % |
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 15 | g/10min |
| density | | ISO1183 | 1.42 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Nominal tensile fracture strain | | ISO527-2 | 25 | % |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 7.0 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 8.0 | kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 8.0 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 8.0 | kJ/m² |
| Poisson's ratio | | ISO527 | 0.35 | |
| Tensile modulus | | ISO527-2 | 3100 | Mpa |
| tensile strength | 屈服 | ISO527-2 | 71.0 | Mpa |
| elongation | 屈服 | ISO527-2 | 14 | % |
| Bending modulus | | ISO178 | 3000 | Mpa |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 160 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 180 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 162 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 96.0 | °C |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 1E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | MD：-40to23°C | ISO11359-2 | 9E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：-- | ISO11359-2 | 1E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：-40to23°C | ISO11359-2 | 9E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：AnnealingTemperature | ISO11359-2 | 160 | °C |
| Linear coefficient of thermal expansion | TD：AnnealingTime-Optional | ISO11359-2 | 30.0 | min/mm |
| Melting temperature | | ISO11357-3 | 178 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Leakage Trace Index | | IEC60112 | 600 | V |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 0.8mm | IEC60695-11-10,-20 | HB | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| FMVSS flammability | | FMVSS302 | B | |
| atomization | F-value(refraction) | ISO6452 | 90 | % |
| atomization | G-value(condensate) | ISO6452 | 3.5E-04 | g |
| Burning rate | 1.00mm | ISO3795 | 24 | mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| Emission | | VDA275 | <8.00 | mg/kg |
| EmissionofOrganicCompounds | | VDA277 | 3.10 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.