Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.04 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 16.0 cm³/10min |
| Shrinkage rate | | ISO 294-4 | 0.40to0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ISO 2039-2 | 110 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D523 | 99 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 33.0 MPa |
| Tensile strain | | ISO 527-2 | 20 % |
| Flexural modulus | | ISO 178 | 2200 MPa |
| bending strength | | ISO 178 | 67.0 MPa |
| Tensile modulus | | ISO 527-2 | 2250 MPa |
| tensile strength | | ISO 527-2 | 43.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/A | 10 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/A | 16 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/A | 24 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 95.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 91.0 °C |
| vicat | | ASTM D15254 | 99.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.