Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 0.940 g/cm³ |
| Water absorption rate | | ISO 62 | <0.010 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Hardness (Shore) | | ISO 868 | 65 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 700 MPa |
| tensile strength | Yield | ISO 527-2 | 22.0 MPa |
| Tensile strain | Break | ISO 527-2 | >200 % |
| WearResistance-Sand-slurrymethod | | | 130 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Surface Resistivity | | IEC 60093 | >1.0E+12 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+14 ohms·cm |
| dielectric strength | | IEC 60243-1 | 45 kV/mm |
| dielectric constant | | IEC 60250 | 2.30 |
| Dissipation Factor | | IEC 60250 | 4E-04 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | | <130 °C |
| melting temperature | | ISO 11357-3 | 135 °C |
| | DIN 53752 | 1.5E-4到2.3E-4 cm/cm/°C |
| specific heat | | DIN 52612 | 1900 J/kg/°C |
| thermal conductivity | | DIN 52612 | 0.40 W/m/K |
| Hot deformation temperature (HDT) | | ISO 306 | 79 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.