Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate - flow | | ASTM D955 | 0.20 到 0.40 % |
| Water absorption rate | | ASTM D570 | 0.12 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | 5VA |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 875 °C |
| Limiting Oxygen Index | | ASTM D2863 | 37 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 62.0 Mpa |
| elongation | | ASTM D638 | 15 % |
| Flexural modulus | | ASTM D790 | 3100 Mpa |
| bending strength | | ASTM D790 | 96.5 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Tensile impact strength | | ASTM D1822 | 53.3 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 3.0E+15 ohms·cm |
| Volume resistivity | | ASTM D257 | 6.0E+15 ohms·cm |
| dielectric strength | | ASTM D149 | 19 KV/mm |
| arc resistance | | ASTM D495 | 0.00 到 120 sec |
| arc resistance | | ASTM D495 | PLC 7 PLC 6 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | 100 到 250 V |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 4 PLC 3 |
| High arc combustion index (HAI) | | UL 746 | > 120 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | 80.0 到 150 mm/min |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | | UL 746 | 30 到 120 sec |
| Hot wire ignition (HWI) | | UL 746 | PLC 2 PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Thermal deformation temperature under load | | ASTM D648 | 138 °C |
| RTI Elec | | UL 746 | 80.0 到 125 °C |
| RTI Imp | | UL 746 | 80.0 到 115 °C |
| RTI | | UL 746 | 80.0 到 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.