Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183/A | 1.10 g/cm³ |
| density | | ISO 1183/A | 1.10 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 12 g/10min |
| melt mass-flow rate | | ISO 1133 | 12 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 75 |
| Shore hardness | | ISO 868 | 75 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| Limiting Oxygen Index | | ISO 4589-2 | 22 % |
| UL flame retardant rating | | UL 94 | V-2 |
| Limiting Oxygen Index | | ISO 4589-2 | 22 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ISO 527-2 | 32.0 MPa |
| Tensile strain | Break | ISO 527-2 | 30 % |
| Flexural modulus | | ISO 178 | 2100 MPa |
| tensile strength | Break | ISO 527-2 | 32.0 MPa |
| Tensile strain | Break | ISO 527-2 | 30 % |
| Flexural modulus | | ISO 178 | 2100 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 3.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 22 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 3.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 3.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 22 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 3.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 43 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 43 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/Af | 69.0 °C |
| vicat | | ISO 306/A50 | 153 °C |
| melting temperature | | ISO 3146 | 165to168 °C |
| Heat distortion temperature | | ISO 75-2/Af | 69.0 °C |
| vicat | | ISO 306/A50 | 153 °C |
| melting temperature | | ISO 3146 | 165to168 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.