PA6 B3 S1 black (3726)
0
- Usages:Furnitureindustrial applications
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.07 g/cm³ | |
| SpiralFlow | 内部方法 | 60.0 cm | |
| Shrinkage rate | ISO294-4 | 1.9 % | |
| ISO294-4 | 1.5 % | ||
| Humidity Absorption | ISO1110 | 2.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | FMVSS302 | <100 mm/min | |
| FlameRating | UL94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179/1eA | 45 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO179/1eU | NoBreak | |
| ISO179/1eU | NoBreak | ||
| Charpy Notched Impact Strength | ISO179/1eA | 55 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO527-2/1 | 2000 MPa | |
| Tensile stress | Yield | ISO527-2/50 | 50.0 MPa |
| Tensile strain | Yield | ISO527-2/50 | 4.5 % |
| Break | ISO527-2/50 | >50 % | |
| Flexural modulus | ISO178 | 1500 MPa | |
| Bending stress | ISO178 | 65.0 MPa | |
| Fracture bending strain | ISO178 | 7.5 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO75-2/A | 48.0 °C | ||
| melting temperature | DINEN11357-1 | 222 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.