ABS 700 SG5 TORAY MALAYSIA

Form：Granules | Grade：High gloss level

Properties:

High gloss

Typical Applications:

Electrical appliancesToyMonitor

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical appliances \| Toy \| Monitor
Properties:	High gloss

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	-30°C,12.7mm	ASTM D256	80	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C,3.20mm	ASTM D256	110	J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	18	kJ/m²
Impact strength of cantilever beam gap	0°C,12.7mm	ASTM D256	110	J/m
	Impact strength of cantilever beam gap	0°C,3.20mm	ASTM D256	160	J/m
		Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	220	J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,12.7mm	ASTM D256	200	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ASTM D790	2300	Mpa
bending strength		ISO 178	77.0	Mpa
bending strength	bending strength		ASTM D790	73.0	Mpa
Tensile strain	Break	ISO 527-2/50	>10	%
elongation	Break	ASTM D638	15	%
tensile strength	Yield	ISO 527-2/50	51.0	Mpa
tensile strength	tensile strength	Yield	ASTM D638	46.0	Mpa
Tensile modulus		ISO 527-2/1	2600	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	86.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,12.7mm	ASTM D648	92.0	°C
thermal conductivity		ASTMC177	0.16	W/m/K
Linear coefficient of thermal expansion	MD	ASTM D696	7.2E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	81.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.04	g/cm³
Water absorption rate	23°C,24hr	ASTM D570	0.30	%
density		ASTM D792	1.05	g/cm³
Shrinkage rate	MD	ASTM D955	0.40-0.60	%
melt mass-flow rate	220°C/10.0kg	ISO 1133	40	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity	23°C	ASTM D257	>1.0E+16	ohms·cm
Surface resistivity		ASTM D257	>1.0E+16	ohms
Dielectric constant	1kHz	ASTM D150	3.10
Dielectric strength		ASTM D149	23	KV/mm
Dissipation factor	1kHz	ASTM D150	6.2E-03
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	114

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.