Polyester, TS

Polyester, TS UP 3620 Hexion Inc.

Properties:
Fillers organic fillers
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	1.8 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	7.5 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	V-0

mechanical properties	Test Method	Test Result
Bending modulus	ISO 178	8000 MPa
bending strength	ISO 178	85.0 MPa
Compressive stress	ISO 604	180 MPa
Tensile modulus	ISO 527-2/1	8500 MPa
tensile strength	ISO 527-2/5	50.0 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	75.0 °C

Physical properties	Test Condition	Test Method	Test Result
density	23°C	ISO 1183	1.72 g/cm³
Apparent density		ISO 60	0.70 g/cm³
Shrinkage rate	--3	ISO 2577	0.75 %
Shrinkage rate	Shrinkage rate	--4	ISO 2577	0.60 %
Water absorption rate		ISO 62	70.0 mg
Shrinkage rate	--3	ISO 2577	0.25 %
Shrinkage rate	Shrinkage rate	--4	ISO 2577	0.25 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+11 ohms
Volume resistivity		IEC 60093	1E+12 ohms·cm
Dielectric strength	1.00mm	IEC 60243-1	30 kV/mm
Relative permittivity	100Hz	IEC 60250	5.00
Dissipation factor	100Hz	IEC 60250	0.020
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H961/30	ISO 2039-1	250 MPa

Supplementary Information	Test Condition	Test Method	Test Result
Compression molding pressure			>10.0 MPa
Compression molding temperature			160to180 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.