Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 1.0 1.0 |
| Water absorption rate | | % | 1.8 1.8 |
| Water absorption rate | | % | 2.8 2.8 |
| density | | g/cm³ | 1.13 1.13 |
| Shrinkage rate | | % | 1.3 1.3 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | | 112 90 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 2500 900 |
| Tensile stress | Yield | MPa | 78.0 40.0 |
| Tensile strain | Yield | % | 4.0 24 |
| Tensile strain | Break | % | 68 >200 |
| Flexural modulus | | MPa | 2500 900 |
| Bending stress | | MPa | 97.0 33.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 5.0 43 |
| Impact strength of simply supported beam without notch | | | 无断裂 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 3E+15 8E+13 |
| dielectric strength | | kV/mm | 37 33 |
| dielectric constant | | | 3.40 3.70 |
| Dissipation Factor | | | 0.020 0.080 |
| CTI | | V | 600 600 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | 154 -- |
| | °C | 56.0 -- |
| | cm/cm/°C | 9.6E-05 9.6E-05 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.