Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.06to1.10 g/cm³ |
| Shrinkage rate | | ISO2577 | 1.2to1.6 % |
| density | | ISO1183 | 1.06to1.10 g/cm³ |
| Shrinkage rate | | | 1.2to1.6 % |
| Water absorption rate | Saturation | ASTMD570 | 8.0 % |
| Water absorption rate | | ISO62 | 8.0 % |
| Water absorption rate | | ASTMD570 | 2.5 % |
| Water absorption rate | | ISO62 | 2.5 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 114 |
| Rockwell hardness | R-Scale | ISO2039-2 | 114 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | Yield | ISO527-2 | 55.0 MPa |
| elongation | Break | ASTMD638 | >50 % |
| Tensile strain | Break | ISO527-2 | >50 % |
| Flexural modulus | | ASTMD790 | 1600 MPa |
| Flexural modulus | | ISO178 | 1600 MPa |
| bending strength | | ASTMD790 | 65.0 MPa |
| Bending stress | | ISO178 | 65.0 MPa |
| tensile strength | Yield | ASTMD638 | 55.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 30 kJ/m² |
| Charpy Notched Impact Strength | | ISO179 | 75 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | NoBreak |
| Impact strength of simply supported beam without notch | | ISO179 | NoBreak |
| Impact strength of cantilever beam gap | | ASTMD256 | 700 J/m |
| Impact strength of cantilever beam gap | | ISO180 | 55 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+13 ohms |
| Volume resistivity | | IEC60093 | 1E+17 ohms·cm |
| dielectric strength | | IEC60243-1 | 100 kV/mm |
| dielectric constant | | IEC60250 | 3.10 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| MaximumUseTemperature-ShortPeaks | | | 180 °C |
| | ASTMD3417 | 218 °C |
| melting temperature | | ISO11357-3 | 218 °C |
| MaximumContinuousUseTemperature | | | 80 °C |
| | ASTMD648 | 170 °C |
| | ISO75-2/B | 170 °C |
| | ASTMD648 | 65.0 °C |
| | ISO75-2/A | 65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.