'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPS A504X90 TORAY JAPAN
693
Form：Granules | Grade：Injection grade
Properties:
Chemical resistanceFlame retardantGlass fiber reinforcedHigh impact resistanceHigh temperature resistan
Typical Applications:
Automotive sectorElectrical componentssporting goodssmall home appliances
Product Description
Certificates(1)
Datasheet
Product Description
| Typical Applications: | Automotive sector | Electrical components | sporting goods | small home appliances |
| Properties: | Chemical resistance | Flame retardant | Glass fiber reinforced | High impact resistance | High temperature resistan |
Certificates
Technical Data Sheet
| other | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| characteristic | 40%加纤.增强.标准 | |||
| Other performance | Test Condition | Test Method | Test Result | Test Unit |
| 320℃,98MPa，Flow长 | TORAY | 100 | ||
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 55 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.28mm | UL 94 | V-0 | |
| Basic Performance | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | 24hr,23℃于水中 | ASTM D-570 | 0.02 | % |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | ASTM D-785 | 122 | R | |
| compressive strength | ASTM D-732 | 80 | ||
| bending strength | 23℃ | ASTM D-790 | 275 | Mpa |
| tensile strength | 23℃ | ASTM D-638 | 207 | Mpa |
| Bending modulus | 23℃ | ASTM D-790 | 13.3 | GPa |
| Impact strength of cantilever beam gap | Unnotched | ASTM D-256 | 55 | KJ/m |
| Notched | ASTM D-256 | 130 | J/m | |
| Elongation at Break | 23℃ | ASTM D-638 | 3.6 | % |
| bending strength | ASTM D790/ISO 178 | 305 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 15.5 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 122 | ||
| tensile strength | ASTM D638/ISO 527 | 200 | kg/cm²(MPa)[Lb/in²] | |
| Elongation at Break | ASTM D638/ISO 527 | 1.8 | % | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 55 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 11 | kg·cm/cm(J/M)ft·lb/in | ||
| Taber abraser | 1000Cycles | ISO 9352 | 50.0 | mg |
| Tensile strain | Break,23°C | ISO 527-2 | 1.8 | % |
| tensile strength | Yield,23°C | ISO 527-2 | 200 | Mpa |
| Bending modulus | 23°C | ISO 178 | 15500 | Mpa |
| bending strength | 23°C | ISO 178 | 305 | Mpa |
| shear strength | 23°C | JISK7214 | 80.0 | Mpa |
| Friction coefficient | 0.25 | |||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Melting temperature | 278 | ℃（℉） | ||
| Hot deformation temperature | HDT | ASTM D648/ISO 75 | >260 | ℃（℉） |
| Combustibility (rate) | UL 94 | V-0 | ||
| Hot deformation temperature | 1.82MPa | ASTM D-648 | >260 | °C |
| Linear coefficient of thermal expansion | Flow | ASTM D-696 | 2.3 | |
| Across Flow | ASTM D-696 | 3.2 | ||
| Melting temperature | DSC | 278 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 260 | °C |
| Melting temperature | ISO 11357-3 | 278 | °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.3E-05 | cm/cm/°C |
| TD | ISO 11359-2 | 3.1E-05 | cm/cm/°C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Taber wear resistance | ASTM D-D1044 | 50 | mg/1000次 | |
| Shrinkage rate | Across Flow | TORAY | 0.70 | % |
| Water absorption rate | ASTM D570/ISO 62 | 0.02 | % | |
| Shrinkage rate | ASTM D955 | 0.36 | % | |
| density | ASTM D792/ISO 1183 | 1.66 | ||
| Friction coefficient | 对铁 | ASTM D-1894 | 0.25 | |
| limiting pv value | TORAY | 815 | KJ/m | |
| Shrinkage rate | Flow | TORAY | 0.20 | % |
| TD:3.00mm2 | Internal Method | 0.80 | % | |
| MD:3.00mm4 | Internal Method | 0.20 | % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.020 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dielectric constant | 10 | ASTM D-150 | 3.8 | |
| Volume resistivity | ASTM D-257 | 10 | Ω.m | |
| ASTM D257/IEC 60093 | 1014 | Ω.cm | ||
| Dielectric constant | ASTM D150/IEC 60250 | 4.2 | ||
| Arc resistance | ASTM D-495 | 127 | ||
| Dissipation factor | 10 | ASTM D-150 | 0.002 | |
| Dielectric strength | ASTM D-149 | 21 | MV/m | |
| Volume resistivity | IEC 60093 | 1E+16 | ohms·cm | |
| Dielectric strength | IEC 60243-1 | 24 | KV/mm | |
| Dielectric constant | 23°C,1MHz | IEC 60250 | 4.20 | |
| Dissipation factor | 23°C,1MHz | IEC 60250 | 2E-03 | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Scale | ISO 2039-2 | 122 | |
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| BarFlowLength | 320°C,1.00mm | Internal Method | 135 | mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.