Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.05 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 4.50 cm³/10min |
| Melt volume flow rate | | ISO 1133 | 48.0 cm³/10min |
| Shrinkage rate | | ISO 294-4 | 0.20to0.60 % |
| Water absorption rate | | ISO 62 | 0.10 % |
| Water absorption rate | | ISO 62 | 0.050 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ISO 489 | 1.570 |
| transmissivity | | ASTM D1003 | 90.0 % |
| Haze ratio | | ASTM D1003 | 2.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | NoBreak |
| Impact strength of cantilever beam gap | | ISO 180/A | 8.0 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | NoBreak |
| Charpy Notched Impact Strength | | ISO 179 | 15 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 1700 MPa |
| tensile strength | | ISO 527-2 | 23.0 MPa |
| Tensile strain | | ISO 527-2 | 80 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+14 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric constant | | IEC 60250 | 2.50 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 72.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 60.0 °C |
| vicat | | ASTM D15253 | 94.0 °C |
| vicat | | ISO 306/B50 | 64.0 °C |
| maximum service temperature | | | 250 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.