PA6 FC-X9201 DSM Additive Manufacturing

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	50.0μm,铸造薄膜	Internal Method	85.0	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Friction coefficient	Itself - Dynamic,铸造薄膜	ISO 8295	0.80
Friction coefficient	Friction coefficient	Itself - Static,铸造薄膜	ISO 8295	1.4
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD	ISO 11359-2	9E-05	cm/cm/°C
Specific heat capacity	--		1550	J/kg/°C
Specific heat capacity	Specific heat capacity	Average:20to150°C		2250	J/kg/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.13	g/cm³
Stickiness		ISO 307	245	cm³/g
Melt viscosity	260°C	Internal Method	2250	Pa·s
film	Test Condition	Test Method	Test Result	Test Unit
Oxygen permeability	0%RH:23°C,50.0μm	DIS15105-1/-2	23	cm³/m²/bar/24hr
Oxygen permeability	Oxygen permeability	85%RH:23°C,50.0μm	DIS15105-1/-2	33	cm³/m²/bar/24hr
film thickness			50	µm
Tensile modulus	50μm,铸造薄膜	Internal Method	465	MPa
tensile strength	Yield,50μm,CastFilm	ISO 527-3	34.0	MPa
tensile strength	tensile strength	50μm,CastFilm	ISO 527-3	94.0	MPa
elongation	Break,50μm,铸造薄膜	ISO 527-3	350	%
Tear strength of pants shape	50μm,CastFilm，MD	ISO 6383-1	32.0	N/mm
Water vapor permeability	23°C,85%RH,50μm,铸造薄膜	DIS15106-1/-3	35	g/m²/24hr
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Puncture resistance	50.0μm	Internal Method	13.2	J/cm
Relative solution viscosity (RSV)	甲酸	Internal Method	3.60

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.