PC/ABS C1200HF RD3D043 SABIC INNOVATIVE US

Form：Granules | Grade：Injection grade

Properties:

High impact resistanceheat-resisting

Typical Applications:

Electrical fieldElectronic fieldAutomotive interior parts

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical field \| Electronic field \| Automotive interior parts
Properties:	High impact resistance \| heat-resisting

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	-30°C, Total Energy	ASTM D3763	54.0	J
Dart impact	Dart impact	23°C, Total Energy	ASTM D3763	54.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.2 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--2	ASTM D638	2270	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2360	Mpa
tensile strength	Yield3	ASTM D638	57.0	Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	55.0	Mpa
elongation	Yield3	ASTM D638	5.0	%
	elongation	Yield	ISO 527-2/50	4.8	%
		elongation	Break3	ASTM D638	150	%
		elongation	elongation	Break	ISO 527-2/50	110	%
Bending modulus	50.0 mm Span4	ASTM D790	2340	Mpa
Bending modulus	Bending modulus	--	ISO 178	2250	Mpa
bending strength	--	ISO 178	86.0	Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	88.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			100 to 110	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Suggested injection volume			30 to 80	%
Hopper temperature			60 to 80	°C
Temperature at the rear of the barrel			250 to 290	°C
Temperature in the middle of the barrel			255 to 295	°C
Temperature at the front of the material cylinder			260 to 300	°C
Spray nozzle temperature			275 to 300	°C
Processing (melt) temperature			275 to 300	°C
Mold temperature			60 to 90	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			40 to 70	rpm
Exhaust hole depth			0.038 to 0.076	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	129	°C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span6	ISO 75-2/Bf	130	°C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	112	°C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span6	ISO 75-2/Af	110	°C
Vicat softening temperature		ISO 306/B50	130	°C
Linear coefficient of thermal expansion	-40 to 40°C，Flow	ASTM E831	7.2E-5	cm/cm/°C
RTI Elec		UL 746	105	°C
RTI Imp		UL 746	80.0	°C
RTI		UL 746	105	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	260°C/5.0 kg	ASTM D1238	19	g/10 min
Melt Volume Flow Rate (MVR)	265°C/5.0 kg	ISO 1133	24.0	cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		UL 746	PLC 2
High arc combustion index		UL 746	PLC 1
Hot wire ignition		UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.