'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
EAA 1410 STYRON US
48
Form：Granules | Grade：Blow molding grade
Properties:
High toughnessHeat sealing performancehigh strength
Typical Applications:
film
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | film |
| Properties: | High toughness | Heat sealing performance | high strength |
Certificates
No Data...
Technical Data Sheet
| optical performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| gloss | 45°,50.8μm | ASTM D2457 | 65 | |
| turbidity | 50.8μm | ASTM D1003 | 5.8 | % |
| 50.8μm | ISO 14782 | 5.8 | % | |
| Basic Performance | Test Condition | Test Method | Test Result | Test Unit |
| melt mass-flow rate | 190℃/2.16kg | ASTM D-1238 | 1.5 | g/10min |
| 190℃/2.16kg | ISO 1133 | 1.5 | g/10min | |
| Monomer content | Internal Method | % | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Elongation at Break | 50.8um，MD | ASTM D-882 | 400 | % |
| 50.8um，MD | ISO 527-3 | 400 | % | |
| 50.8um，TD | ISO 527-3 | 470 | % | |
| Dart impact | 50.8um | ASTM D-1709B | 580 | g |
| 50.8um | ISO 7765-1/B | 580 | g | |
| Elmendorf tear strength | 50.8um，TD | ASTM D-1922 | 510 | g |
| 50.8um，MD | ASTM D-1922 | 380 | g | |
| 50.8um，MD | ISO 6383-2 | 1700 | N | |
| 50.8um，TD | ISO 6383-2 | 2300 | N | |
| tensile strength | Yield,Compression Molded | ASTM D-638 | 8.39 | MPa |
| Yield,Compression Molded | ISO 527-2/508 | 8.39 | MPa | |
| Compression Molded，Break | ASTM D-638 | 22.5 | MPa | |
| Compression Molded，Break | ISO 527-2/508 | 22.5 | MPa | |
| 50.8um，Yield,MD | ASTM D-882 | 11.8 | MPa | |
| 50.8um，Yield,TD | ASTM D-882 | 10.9 | MPa | |
| 50.8um，Yield,TD | ISO 527-3 | 10.9 | MPa | |
| 50.8um，Yield,MD | ISO 527-3 | 11.8 | MPa | |
| 50.8um，TD,Break | ASTM D-882 | 38.1 | MPa | |
| 50.8um，MD,Break | ASTM D-882 | 37.9 | MPa | |
| 50.8um，MD,Break | ISO 527-3 | 37.9 | MPa | |
| 50.8um，TD,Break | ISO 527-3 | 38.1 | MPa | |
| Elongation at Break | 50.8um，TD | ASTM D-882 | 470 | % |
| tensile strength | Yield,Compression Molded4 | ASTM D638 | 8.39 | Mpa |
| Yield,Compression Molded | ISO 527-2/508 | 8.39 | Mpa | |
| Break,Compression Molded4 | ASTM D638 | 22.5 | Mpa | |
| Break,Compression Molded | ISO 527-2/508 | 22.5 | Mpa | |
| elongation | Break,Compression Molded4 | ASTM D638 | 640 | % |
| Break,Compression Molded | ISO 527-2/508 | 640 | % | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Vicat softening temperature | ASTM D-1525 | 81.1 | ℃ | |
| ISO 306 | 81.1 | ℃ | ||
| Melting temperature | Internal Method | 97.8 | ℃ | |
| Vicat softening temperature | ASTMD1525 | 81.1 | °C | |
| Melting temperature | Internal Method | 97.8 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| melt mass-flow rate | 190°C/2.16kg | ASTMD1238 | 1.5 | g/10min |
| Content of comonomer | Internal Method | 9.7 | % | |
| film | Test Condition | Test Method | Test Result | Test Unit |
| tensile strength | TD:Yield,51μm | ASTM D882 | 10.9 | Mpa |
| MD:Yield,51μm | ISO 527-3 | 11.8 | Mpa | |
| TD:Yield,51μm | ISO 527-3 | 10.9 | Mpa | |
| MD:Break,51μm | ASTMD882 | 37.9 | Mpa | |
| TD:Break,51μm | ASTMD882 | 38.1 | Mpa | |
| elongation | MD:Break,51μm | ASTMD882 | 400 | % |
| TD:Break,51μm | ASTMD882 | 470 | % | |
| Dart impact | 51μm | ASTMD1709B | 580 | g |
| Elmendorf tear strength | MD:51μm | ASTM D1922 | 380 | g |
| TD:51μm | ASTM D1922 | 510 | g | |
| MD:51μm | ISO 6383-2 | 1700 | N | |
| TD:51μm | ISO 6383-2 | 2300 | N | |
| tensile strength | MD:Yield,51μm | ASTM D882 | 11.8 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.