Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO2577 | 0.50到0.70 % |
| Shrinkage rate | | ISO2577 | 0.50到0.70 % |
| Water absorption rate | | ISO62 | 0.50 % |
| Water absorption rate | | ISO62 | 0.20 % |
| density | | ISO1183 | 1.19 g/cm³ |
| Melt volume flow rate | | ISO1133 | 25.0 cm³/10min |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | 5VB |
| UL flame retardant rating | | UL94 | 5VA |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISO Shortcut | | | PC+ABS-FR(40 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| MeltViscosity | | ISO11443-A | 170 Pa·s |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 2600 MPa |
| Tensile stress | | ISO527-2/50 | 60.0 MPa |
| Tensile stress | | ISO527-2/50 | 50.0 MPa |
| Tensile strain | | ISO527-2/50 | 4.0 % |
| Tensile strain | | ISO527-2/50 | >30 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/A | 35 kJ/m² |
| | ISO180 | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | IEC60250 | 7E-03 |
| dielectric strength | | IEC60243-1 | 30 kV/mm |
| | IEC60250 | 3.20 |
| | IEC60250 | 3.10 |
| Dissipation Factor | | IEC60250 | 5E-03 |
| Surface Resistivity | | IEC60093 | 1E+16 ohms |
| Volume resistivity | | IEC60093 | 1E+16 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 95.0 °C |
| | ISO75-2/A | 85.0 °C |
| vicat | | ISO306/B120 | 105 °C |
| | ISO11359-2 | 7.6E-05 cm/cm/°C |
| | ISO11359-2 | 8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare