PA6 73M30 NC010 DUPONT USA

152

Form：Granules | Grade：Enhanced level

Properties:

Thermal stabilityEasy electroplating

Typical Applications:

Automotive sectorElectronic fieldElectrical field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive sector \| Electronic field \| Electrical field
Properties:	Thermal stability \| Easy electroplating

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			低翘曲性热稳定性
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	110	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	85	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.9mm	UL 94	HB
Flammability level	0.8mm	IEC 60695-11-10,-20	HB
FMVSS flammability		FMVSS302	SE
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	4800	Mpa
tensile strength	Break	ISO 527-2	82.0	Mpa
Bending modulus		ISO 178	4800	Mpa
Tensile creep modulus	1000hr	ISO 899-1	--	Mpa
Tensile modulus		ASTM D638/ISO 527	4800	kg/cm²(MPa)[Lb/in²]
Tensile strain	Break	ISO 527-2	15	%
Tensile creep modulus	1hr	ISO 899-1	--	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：55to160°C	ISO 11359-2	1.1E-04	cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	5.7E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：--	ISO 11359-2	6.5E-05	cm/cm/°C
			Linear coefficient of thermal expansion	MD：55to160°C	ISO 11359-2	8.9E-05	cm/cm/°C
				Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	5.6E-05	cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：--	ISO 11359-2	6.3E-05	cm/cm/°C
Melting temperature		ISO 11357-3	221	°C
Vicat softening temperature		ISO 306/B50	210	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	80.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	195	°C
Combustibility (rate)		UL 94	HB
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	2.1	%
Shrinkage rate		ASTM D955	0.9	%
density		ASTM D792/ISO 1183	1.35
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	6.3	%
Shrinkage rate	MD	ISO 294-4	0.90	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	0.90	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA6 73M30 NC010 DUPONT USA

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index