PPS 4332L6 CELANESE USA

Form：Granules | Grade：Injection grade

Properties:

Flame retardant

Typical Applications:

Automotive sectorElectronic fieldElectrical field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive sector \| Electronic field \| Electrical field
Properties:	Flame retardant

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	30	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	10	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1A/1	21500	Mpa
tensile strength	Break	ISO 527-2/1A/5	160	Mpa
tensile strength	tensile strength	Break	ISO 527-2/1A/5	160	MPa
bending strength	23°C	ISO 178	260	Mpa
Bending modulus	23°C	ISO 178	21000	Mpa
Tensile modulus		ISO 527-2/1A/1	21500	MPa
Impact strength of simply supported beam without notch	23°C	ISO 179/1eA	10	kJ/m²
bending strength	23°C	ISO 178	260	MPa
Bending modulus	23°C	ISO 178	21000	MPa
Tensile strain	Break	ISO 527-2/1A/5	1.2	%
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	30	kJ/m²
Tensile strain	Break	ISO 527-2/1A/5	1.2	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	flow	ISO 11359-2	0.000012	cm/cm/°C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	220	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	270	°C
Linear coefficient of thermal expansion	TD	ISO 11359-2	3.1E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD	ISO 11359-2	1.4E-05	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Transverse	ISO 11359-2	0.000053	cm/cm/°C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	229	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	250	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Saturation,23°C	ISO 62	0.020	%
Shrinkage rate	TD	ISO 294-4	0.30-0.70	%
density		ISO 1183	1.95	g/cm³
density	density		ASTM D792	1.95	g/cm³
Shrinkage rate	MD	ISO 294-4	0.20-0.60	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.