'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PA66 CM3004G-30 RD TORAY JAPAN
116
Form：Granules | Grade：Halogen-free flame retardant grade
Properties:
Flame retardantGlass fiber reinforced Glass fiber reinforced bFiller: Glass fiber reinfFlame retardant gradehalogen-containing 30%Filler by weight
Typical Applications:
Office suppliesAutomotive sectorbuilding materialsElectronic fieldElectrical field
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Office supplies | Automotive sector | building materials | Electronic field | Electrical field |
| Properties: | Flame retardant | Glass fiber reinforced | Glass fiber reinforced b | Filler: Glass fiber reinf | Flame retardant grade | halogen-containing | 30% | Filler by weight |
Certificates
No Data...
Technical Data Sheet
| Other performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| filler content | 无水｜30 | wt% | ||
| 1.3%水｜- | wt% | |||
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Charpy Notched Impact Strength | -40°C | kJ/m² | 7.0 | -- |
| 23°C | kJ/m² | 9.5 | 14 | |
| Impact strength of simply supported beam without notch | 23°C | kJ/m² | 65 | 70 |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.40mm | V-0 | -- | |
| Basic Performance | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | 23℃，24hr | ASTM D-570 | 1.3%水｜- | % |
| 23℃，24hr | ASTM D-570 | 无水｜0.4 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Bending modulus | 23℃ | ASTM D-790 | 1.3%水｜65000 | kg/cm2 |
| 23℃ | ASTM D-790 | 无水｜93200 | kg/cm2 | |
| bending strength | 23℃ | ASTM D-790 | 1.3%水｜2000 | kg/cm2 |
| 23℃ | ASTM D-790 | 无水｜2490 | kg/cm2 | |
| Elongation at Break | 23℃ | ASTM D-638 | 1.3%水｜5 | % |
| 23℃ | ASTM D-638 | 无水｜5 | % | |
| tensile strength | 23℃，Break | ASTM D-638 | 1.3%水｜1350 | kg/cm2 |
| 23℃，Break | ASTM D-638 | 无水｜1640 | kg/cm2 | |
| Impact strength of cantilever beam gap | 23℃，Unnotched1/8 | 1.3%水｜70 | kg.cm/cm | |
| 23℃，Unnotched1/8 | 无水｜65 | kg.cm/cm | ||
| Tensile strain | Break,-40°C | % | 2.5 | -- |
| Break,23°C | % | 3.0 | 3.0 | |
| Break,80°C | % | 4.5 | -- | |
| Bending modulus | -40°C | MPa | 10200 | -- |
| 23°C | MPa | 9300 | 6500 | |
| tensile strength | -40°C | MPa | 190 | -- |
| 23°C | 165 | MPa | ||
| 80°C | MPa | 110 | -- | |
| Bending modulus | 80°C | MPa | 5500 | -- |
| bending strength | -40°C | MPa | 275 | -- |
| 23°C | 250 | MPa | ||
| 80°C | MPa | 150 | -- | |
| Taber abraser | 1000Cycles | mg | 26.0 | -- |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | ASTM D-696 | 1.3%水｜- | ||
| Hot deformation temperature | 18.6kg/cm2 | ASTM D-648 | 无水｜251 | °C |
| Linear coefficient of thermal expansion | ASTM D-696 | 无水｜2 | 10-5cm/cm.℃ | |
| Hot deformation temperature | 18.6kg/cm2 | ASTM D-648 | 1.3%水｜- | °C |
| Melting temperature | 差示扫描测热计DSC法 | 265 | °C | |
| UL-94 flame retardant grade | UL 94 | 无水｜V-0 | ||
| UL 94 | 1.3%水｜- | |||
| Hot deformation temperature | 0.45MPa,Unannealed | °C | 251 | -- |
| Melting temperature | °C | 265 | -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 2E-05 | -- |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| density | ASTM D-792 | 1.3%水｜- | ||
| ASTM D-792 | 无水｜1.59 | |||
| 23°C | g/cm³ | 1.59 | -- | |
| Shrinkage rate | TD:3.00mm3 | % | 0.60-0.90 | -- |
| MD:3.00mm4 | % | 0.20-0.50 | -- | |
| Water absorption rate | 23°C,24hr | % | 0.60 | -- |
| Saturation,23°C | % | 4.0 | -- | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Volume resistivity | ASTM D-257 | 无水｜8×1014 | Ω.cm | |
| Arc resistance | 1/8" | ASTM D-495 | 1.3%水｜- | S |
| 1/8" | ASTM D-495 | 无水｜70-80 | S | |
| Dissipation factor | 106Hz | ASTM D-150 | 1.3%水｜- | |
| 106Hz | ASTM D-150 | 无水｜0.003-0.009 | ||
| Compared to the Leakage Traceability Index (CTI) | UL 746 | 1.3%水｜- | V | |
| UL 746 | 无水｜200 | V | ||
| Dielectric strength | 1/8" | ASTM D-149 | 1.3%水｜33 | KV/mm |
| 1/8" | ASTM D-149 | 无水｜38 | KV/mm | |
| Volume resistivity | ASTM D-257 | 1.3%水｜8×1013 | Ω.cm | |
| Dielectric constant | 23°C,1MHz | 0.0100 | -- | |
| Arc resistance | sec | 70.0 | -- | |
| Volume resistivity | ohms·cm | 1E+15 | 1E+13 | |
| Dielectric strength | kV/mm | 38 | 33 | |
| Dielectric constant | 23°C,1kHz | 4.00 | -- | |
| Compared to the anti leakage trace index | CTI | V | PLC 3 | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Sale,23°C | 121 | -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.