Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Spiral flow length | | 出光法 | 0.13 CM |
| processability | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D-955 | 2.0 |
| Shrinkage rate | | ASTM D-955 | 6.0 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D-570 | 0.13 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile failure rate | | ISO R-527 (ASTM D-638) | 4 % |
| Tensile elasticity | | ISO R-527 (ASTM D-638) | 5700(58000) MPa(KG/cm |
| Tensile strength | | ISO R-527 (ASTM D-638) | 100(1000) MPa(KG/cm |
| | ISO 178 (ASTM D-790) | 140(1400) Mpa |
| IZOD impact strength | | ISO 180 (ASTM D-256) | 13(14) KJ/m |
| Rockwell hardness | | ISO 2039-2 (ASTM D-785) | M91 |
| | ISO 178 (ASTM D-790) | 5880(60000) MPa(KG/cm |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| permittivity | | ASTM D-150 | 3.25 |
| Inherent resistance of volume | | ASTM D-257 | ＜10 Ω·cm |
| Induced positive connection | | ASTM D-150 | 8×10 |
| Insulation breakdown voltage | | ASTM D-149 | ＜22 KV/mm |
| permittivity | | ASTM D-150 | 3.15 |
| arc resistance | | ASTM D-495 | 110 sec |
| Induced positive connection | | ASTM D-150 | 9×10 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Load deflection temperature | | ISO 75(ASTM D-648) | 139 °C |
| combustibility | | UL 94 | V-2 |
| linear expansion coefficient | | ASTM D-696 | 2.5 |
| vicat | | ISO 306 | 150 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.