Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 19 g/10min |
| Melt volume flow rate | | ISO 1133 | 18.0 cm3/10min |
| Water absorption rate | | ISO 62 | 0.50 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 80 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ColorNumber | | | CF2001 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Wear factor | | JISK7218 | 4000 10^-8mm³/N·m |
| Tensile modulus | | ISO 527-2 | 2250 Mpa |
| tensile strength | | ISO 527-2 | 54.0 Mpa |
| Nominal tensile fracture strain | | ISO 527-2 | 20 % |
| Flexural modulus | | ISO 178 | 2100 Mpa |
| bending strength | | ISO 178 | 72.0 Mpa |
| coefficient of friction | | JISK7218 | 0.38 |
| coefficient of friction | | JISK7218 | 0.75 |
| Wear factor | | JISK7218 | <1.0 10^-8mm³/N·m |
| Wear factor | | JISK7218 | 600 10^-8mm³/N·m |
| Wear factor | | JISK7218 | 1500 10^-8mm³/N·m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 5E+15 ohms |
| Volume resistivity | | IEC 60093 | 7E+13 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | 内部方法 | 1.2E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | 内部方法 | 1.2E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices