ABS

ABS CR-250 LG CHEM KOREA

Properties:
High impact resistance Resistance to compound e
Compare

Technical Data Sheet

machinability	Test Condition	Test Method	Test Result
Shrinkage rate		ASTM D-955	0.3-0.5 %

Basic Performance	Test Condition	Test Method	Test Result
melt mass-flow rate	220℃ 10kg	ASTM D-1238	21 g/10min

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	15mm/min	ASTM D-790	25500 kg/cm2
Impact strength of cantilever beam gap	1/4〃 Notched	ASTM D-256	24 kg.cm/cm
Rockwell hardness		ASTM D-785	112 R scale
tensile strength	50mm/min	ASTM D-638	550 kg/cm2
Elongation at Break	50mm/min	ASTM D-638	20 %
bending strength	15mm/min	ASTM D-790	870 kg/cm2

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	18.5kg/cm2	ASTM D-648	92 °C
Vicat softening temperature	1KG	ASTM D-1525	103 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.