Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting mixed viscosity | | Brookfield | 325 cP |
| Thermosetting mixed viscosity | | Brookfield | 1450 cP |
| Thermosetting mixed viscosity | | Brookfield | 740 cP |
| Thermosetting mixed viscosity | | Brookfield | 60to120 min |
| Thermosetting mixed viscosity | | Brookfield | 120to170 hr |
| Thermosetting mixed viscosity | | Brookfield | 6.0to7.0 min |
| Thermosetting mixed viscosity | | Brookfield | 5.0-6.0 min |
| Thermosetting components | | | 按重量计算的混合比:70.按容量计算的混合比:79 |
| Thermosetting components | | | 按重量计算的混合比:100.按容量计算的混合比:100 |
| Thermosetting components | Shelf Life | | 26 wk |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 0.791 cm³/g |
| density | | | 0.060 % |
| density | | | 1.18 g/cm³ |
| density | | ASTM D792 | 1.30 g/cm³ |
| density | | | 1.33 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 78to82 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTM D638 | 42.2 MPa |
| elongation | Yield | ASTM D638 | 21 % |
| Flexural modulus | | ASTM D790 | 1940 MPa |
| bending strength | | ASTM D790 | 69.8 MPa |
| Tensile modulus | | ASTM D638 | 1720 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 31 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | ASTM D150 | 0.014 |
| dielectric constant | | ASTM D150 | 3.24 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 85.6 °C |
| Heat distortion temperature | | ASTM D648 | 75.6 °C |
| ball-indentation hardness | | IEC 60695-10-2 | 通过 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.