Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | 0.35 % |
| density | | ISO1183 | 1.54 g/cm³ |
| Melt volume flow rate | | ISO1133 | 14.0 cm³/10min |
| Shrinkage rate | | ISO2577 | 1.4 % |
| Shrinkage rate | | ISO2577 | 1.4 % |
| Water absorption rate | | ISO62 | 0.18 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 175 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | 内部方法 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 4200 MPa |
| Tensile strain | Break | ISO527-2/5 | 3.0 % |
| Tensile stress | Break | ISO527-2/5 | 50.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 25 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 3.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 3.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 25 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | IEC60112 | 250 V |
| Surface Resistivity | | IEC60093 | >1.0E+14 ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| | IEC60250 | 4.50 |
| | IEC60250 | 4.30 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 185 °C |
| | ISO75-2/A | 80.0 °C |
| vicat | | ISO306/B50 | 195 °C |
| melting temperature | | ISO11357-3 | 220到225 °C |
| | ISO11359-2 | 1.1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.