'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC/PBT 5720U-1001 SABIC INNOVATIVE US
158
Form：Granules | Grade：Cold resistant grade
Properties:
Chemical resistanceLow temperature impact re
Typical Applications:
Plastic bagLighting applicationsHousehold daily necessities
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Plastic bag | Lighting applications | Household daily necessities |
| Properties: | Chemical resistance | Low temperature impact re |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 47 | kJ/m² |
| 23°C | ISO 179/1eA | 55 | kJ/m² | |
| Dart impact | -40°C, Energy at Peak | ASTM D3763 | 49.0 | J |
| -40°C, Total Energy | ASTM D3763 | 59.0 | J | |
| -30°C, Energy at Peak | ASTM D3763 | 49.0 | J | |
| -30°C, Total Energy | ASTM D3763 | 61.0 | J | |
| -20°C, Energy at Peak | ASTM D3763 | 41.0 | J | |
| -20°C, Total Energy | ASTM D3763 | 53.0 | J | |
| 23°C, Energy at Peak | ASTM D3763 | 44.0 | J | |
| 23°C, Total Energy | ASTM D3763 | 54.0 | J | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| tensile strength | Break5 | ASTM D638 | 48.0 | Mpa |
| Break | ISO 527-2/5 | 43.0 | Mpa | |
| elongation | Yield7 | ASTM D638 | 4.6 | % |
| Yield6 | Internal Method | 4.6 | % | |
| tensile strength | Break6 | Internal Method | 47.0 | Mpa |
| Break7 | ASTM D638 | 50.0 | Mpa | |
| Yield | ISO 527-2/50 | 47.0 | Mpa | |
| Yield | ISO 527-2/5 | 44.0 | Mpa | |
| Yield7 | ASTM D638 | 44.0 | Mpa | |
| Yield6 | Internal Method | 45.0 | Mpa | |
| Yield5 | ASTM D638 | 47.0 | Mpa | |
| Tensile modulus | -- | ISO 527-2/1 | 1790 | Mpa |
| --4 | ASTM D638 | 1810 | Mpa | |
| --3 | Internal Method | 1830 | Mpa | |
| --2 | ASTM D638 | 1830 | Mpa | |
| elongation | Yield5 | ASTM D638 | 4.0 | % |
| Yield | ISO 527-2/5 | 4.1 | % | |
| Yield | ISO 527-2/50 | 4.6 | % | |
| Break7 | ASTM D638 | 120 | % | |
| Break6 | Internal Method | 110 | % | |
| Break5 | ASTM D638 | 120 | % | |
| Break | ISO 527-2/5 | 110 | % | |
| Break | ISO 527-2/50 | 120 | % | |
| Bending modulus | 50.0 mm Span8 | ASTM D790 | 1660 | Mpa |
| --9 | ISO 178 | 1860 | Mpa | |
| bending strength | --9,10 | ISO 178 | 71.0 | Mpa |
| Yield, 50.0 mm Span8 | ASTM D790 | 70.0 | Mpa | |
| Break, 50.0 mm Span8 | ASTM D790 | 69.0 | Mpa | |
| injection | Test Condition | Test Method | Test Result | Test Unit |
| drying temperature | 110 | °C | ||
| drying time | 4.0 to 6.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 50 to 80 | % | ||
| Temperature at the rear of the barrel | 245 to 265 | °C | ||
| Temperature in the middle of the barrel | 250 to 270 | °C | ||
| Temperature at the front of the material cylinder | 255 to 275 | °C | ||
| Spray nozzle temperature | 255 to 270 | °C | ||
| Processing (melt) temperature | 260 to 275 | °C | ||
| Mold temperature | 65 to 90 | °C | ||
| Back pressure | 0.300 to 0.700 | Mpa | ||
| Screw speed | 50 to 80 | rpm | ||
| Exhaust hole depth | 0.013 to 0.020 | mm | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span12 | ISO 75-2/Bf | 109 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 83.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 95.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span12 | ISO 75-2/Af | 87.0 | °C | |
| 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 108 | °C | |
| 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 117 | °C | |
| Vicat softening temperature | -- | ASTM D152513 | 119 | °C |
| -- | ISO 306/B120 | 122 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 95°C | ASTM E831 | 9.8E-5 | cm/cm/°C |
| Flow : -30 to 80°C | ISO 11359-2 | 9.8E-5 | cm/cm/°C | |
| Across Flow : -40 to 95°C | ASTM E831 | 1.0E-4 | cm/cm/°C | |
| Across Flow : -30 to 80°C | ISO 11359-2 | 1.0E-4 | cm/cm/°C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.080 | % |
| Saturation, 23°C | ISO 62 | 0.28 | % | |
| Shrinkage rate | 3.20 mm，Flow | Internal Method | 1.0 - 1.2 | % |
| Melt Volume Flow Rate (MVR) | 265°C/5.0 kg | ISO 1133 | 18.0 | cm3/10min |
| 265°C/2.16 kg | ISO 1133 | 6.00 | cm3/10min | |
| 250°C/5.0 kg | ISO 1133 | 10.0 | cm3/10min | |
| 250°C/2.16 kg | ISO 1133 | 3.00 | cm3/10min | |
| melt mass-flow rate | 250°C/2.16 kg | ISO 1133 | 3.0 | g/10 min |
| 266°C/5.0 kg | ASTM D1238 | 20 | g/10 min | |
| 265°C/2.16 kg | ASTM D1238 | 6.0 | g/10 min | |
| 250°C/5.0 kg | ASTM D1238 | 11 | g/10 min | |
| 250°C/2.16 kg | ASTM D1238 | 3.8 | g/10 min | |
| Specific volume | ASTM D792 | 0.850 | cm³/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.