Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO294-4 | 0.50to0.70 % |
| Shrinkage rate | | ISO294-4 | 0.25to0.45 % |
| Water absorption rate | | ISO62 | 0.30 % |
| density | | ISO1183 | 1.54 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 800 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 800 °C |
| Limiting Oxygen Index | | ASTMD2863 | 28 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Dimensional Stability | | | 60.0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2/5 | 125 MPa |
| Tensile stress | | ISO527-2/5 | 80.0 MPa |
| Tensile stress | | ISO527-2/5 | 60.0 MPa |
| Tensile stress | | ISO527-2/5 | 50.0 MPa |
| Tensile stress | | ISO527-2/5 | 40.0 MPa |
| Tensile strain | | ISO527-2/5 | 2.0 % |
| Tensile strain | | ISO527-2/5 | 4.5 % |
| Tensile strain | | ISO527-2/5 | 6.0 % |
| Tensile modulus | | ISO527-2/1 | 11000 MPa |
| Tensile modulus | | ISO527-2/1 | 7400 MPa |
| Tensile modulus | | ISO527-2/1 | 5100 MPa |
| Tensile modulus | | ISO527-2/1 | 4200 MPa |
| Tensile modulus | | ISO527-2/1 | 3600 MPa |
| Tensile strain | | ISO527-2/5 | 7.0 % |
| Tensile strain | | ISO527-2/5 | 7.5 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 35 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 40 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | IEC60112 | 400 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 215 °C |
| | ISO75-2/A | 185 °C |
| Continuous use temperature | | | 115 °C |
| vicat | | ISO306/B50 | 195 °C |
| | ISO11359-2 | 1.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.