ABS TAIRILAC® AG15A3 FCFC TAIWAN
1922
- Properties:High glossHigh rigidity
- Usages:Electrical appliancesElectronic fieldElectrical fieldHousehold goods
- Certificates:MSDSULTDSProcessingMSDSULRoHSSVHCEnvironmental
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.4-0.7 | % |
| Melt mass flow rate | 200°C/5.0 kg | ASTM D-1238 | 2.2 | g/10min |
| 220°C/10.0 kg | ASTM D-1238 | 22 | g/10min | |
| density | ASTM D-792 | 1.05 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Cantilever beam without notch impact strength | 23℃,6.35mm | ASTM D-256 | 220 | J/m |
| tensile strength | 23℃ | ASTM D-638 | 46 | Mpa |
| Rockwell hardness | R级,23℃ | ASTM D-785 | 108 | |
| Bending modulus | 23℃ | ASTM D-790 | 2650 | Mpa |
| bending strength | 23℃ | ASTM D-790 | 78 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ASTM D-1525 | 99 | °C | |
| Hot deformation temperature | 1.8MPa,退火,12.7mm | ASTM D-648 | 85 | °C |
| 1.8MPa,退火 | ASTM D-648 | 95 | °C | |
| Flame retardant grade | 1.50 mm, All Colors | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.