PP Copolymer TRANSMARE® 5CGF30

Properties:
Filler
glass fiber reinforced material
30%
filler by volume
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO1183	1.11 g/cm³
melt mass-flow rate		ISO1133	22 g/10min
melt mass-flow rate	melt mass-flow rate		ISO1133	1.4 g/10min
Melt volume flow rate		ISO1133	1.50 cm³/10min
Moisture content		内部方法	<0.20 %

hardness	Test Condition	Test Method	Test Result
		ISO868	70

flammability	Test Condition	Test Method	Test Result
burning rate		FMVSS302	<100 mm/min

Mechanical properties	Test Condition	Test Method	Test Result
Tensile stress		ISO527-2/50	71.0 MPa
	Tensile stress		ISO527-2/50	71.0 MPa
	Tensile stress	Tensile stress		ISO527-2	71.0 MPa
TensileStrain		ISO527-2/50	5.0 %
Tensile strain		ISO527-2/50	6.0 %
Tensile modulus		ISO527-2/1	5420 MPa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO179/A	9.0 kJ/m²
	Charpy Notched Impact Strength		ISO179/A	11 kJ/m²
		Charpy Notched Impact Strength		ISO179/A	12 kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO179/A	19 kJ/m²
Impact strength of cantilever beam gap		ISO180/A	12 kJ/m²
	Impact strength of cantilever beam gap		ISO180/A	14 kJ/m²
		Impact strength of cantilever beam gap		ISO180/A	16 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO180/A	19 kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.