Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.12 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 1.0to20 g/10min |
| melt mass-flow rate | | ASTM D1238 | 1.0to10 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | Shore A | ASTM D2240 | 85 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Injection | ASTM D412 | 20.7 MPa |
| Flexural modulus | Injection | ASTM D790 | 29.0 MPa |
| Taber abraser | | ASTM D1044 | 30.0 mg |
| wear resistance | | DIN 53516 | 25 mm³ |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| compression set | | ASTM D395B | 45 % |
| tensile strength | | ASTM D412 | 9.65 MPa |
| tensile strength | | ASTM D412 | 21.4 MPa |
| tensile strength | | ASTM D412 | 35.9 MPa |
| elongation | Break | ASTM D412 | 530 % |
| tear strength | | ASTM D624 | 110 kN/m |
| compression set | | ASTM D395B | 25 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | 内部方法 | -38.0 °C |
| vicat | | ASTM D1525 | 100 °C |
| vicat | | 内部方法 | 66 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.