GPPS GP5250 FORMOSA NINGBO

153

Form：Granules | Grade：Injection grade

Properties:

currency

Typical Applications:

Food packagingFood containersToyMonitorAudiotapechipMakeup productscontainer

Supplier(1)

Product Description

Certificates(2)

Datasheet

Alternative Model(23)

Product Description

Typical Applications:	Food packaging \| Food containers \| Toy \| Monitor \| Audiotape \| chip \| Makeup products \| container
Properties:	currency

Certificates

SGS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C,6.35mm	ISO 180	17	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	17	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	23°C	ASTM D638	42.2	Mpa
tensile strength	tensile strength	Yield,23°C	ISO 527-2	42.0	Mpa
elongation	Break,23°C	ASTM D638	2.0	%
Tensile strain	Break,23°C	ISO 527-2	2.0	%
Bending modulus	23°C	ASTM D790	3330	Mpa
Bending modulus	Bending modulus	23°C	ISO 178	3330	Mpa
bending strength	23°C	ASTM D790	78.0	Mpa
bending strength	bending strength	23°C	ISO 178	78.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Annealed,3.18mm	ASTM D648	87.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,3.18mm	ISO 75-2/A	87.0	°C
Vicat softening temperature		ASTM D1525	94.0	°C
Vicat softening temperature	Vicat softening temperature		ISO 306/B	94.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.04	g/cm³
density	density	23°C	ISO 1183	1.04	g/cm³
melt mass-flow rate	200°C/5.0kg	ASTM D1238	7.0	g/10min
melt mass-flow rate	melt mass-flow rate	200°C/5.0kg	ISO 1133	7.0	g/10min
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Residual Monomer			<700	ppm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.