PA46 TS200F10 DSM JAPAN

Form：Granules | Grade：Injection grade

Properties:

heat-resistingFlame retardant

Typical Applications:

Home appliance componentsElectronic and electrical components

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Home appliance components \| Electronic and electrical components
Properties:	heat-resisting \| Flame retardant

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	12	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-40°C	ISO 180/1A	11	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	65	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	12	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	11	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Flammability level		UL 94	HB
Flammability level	Flammability level		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--	ISO 527-2	10000	Mpa
	Tensile modulus	120°C	ISO 527-2	5500	Mpa
		Tensile modulus	160°C	ISO 527-2	5000	Mpa
		Tensile modulus	Tensile modulus	180°C	ISO 527-2	4400	Mpa
Bending modulus	160°C	ISO 178	3900	Mpa
	Bending modulus	120°C	ISO 178	4700	Mpa
	Bending modulus	Bending modulus	--	ISO 178	9000	Mpa
Tensile strain	Break, 200°C	ISO 527-2	7.5	%
	Tensile strain	Break, 180°C	ISO 527-2	7.5	%
		Tensile strain	Break, 160°C	ISO 527-2	7.5	%
			Tensile strain	Break, 120°C	ISO 527-2	7.5	%
			Tensile strain	Tensile strain	Break	ISO 527-2	4.0	%
tensile strength	Break, 200°C	ISO 527-2	90.0	Mpa
	tensile strength	Break, 180°C	ISO 527-2	95.0	Mpa
		tensile strength	Break, 160°C	ISO 527-2	100	Mpa
			tensile strength	Break, 120°C	ISO 527-2	110	Mpa
			tensile strength	tensile strength	Break	ISO 527-2	210	Mpa
Tensile modulus	200°C	ISO 527-2	4000	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	6.0E-5	cm/cm/°C
RTI Elec	0.8 mm	UL 746	65.0	°C
Thermal Index - 5000 hr		IEC 60216	152	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.5E-5	cm/cm/°C
Melting temperature		ISO 11357-3	295	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	290	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	290	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.41	g/cm³
Shrinkage rate	横向Flow	ISO 294-4	1.3	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.50	%
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.6	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	35	KV/mm
Relative permittivity	100 Hz	IEC 60250	4.40
Relative permittivity	Relative permittivity	1 MHz	IEC 60250	4.00
Compared to the anti leakage trace index		IEC 60112	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.